Operando ESR observation in thermally activated delayed fluorescent organic light

Scientific Reports volume 13, Article number: 11109 (2023) Cite this article

372 Accesses

Metrics details

Organic light-emitting diodes (OLEDs) using thermally activated delayed fluorescence (TADF) materials have advantages over OLEDs using conventional fluorescent materials or high-cost phosphorescent materials, including higher efficiency and lower cost. To attain further high device performance, clarifying internal charge states in OLEDs at a microscopic viewpoint is crucial; however, only a few such studies have been performed. Here, we report a microscopic investigation into internal charge states in OLEDs with a TADF material by electron spin resonance (ESR) at a molecular level. We observed operando ESR signals of the OLEDs and identified their origins due to a hole-transport material PEDOT:PSS, gap states at an electron-injection layer, and a host material CBP in the light-emitting layer by performing density functional theory calculation and studying thin films used in the OLEDs. The ESR intensity varied with increasing applied bias before and after the light emission. We find leakage electrons in the OLED at a molecular level, which is suppressed by a further electron-blocking layer MoO3 between the PEDOT:PSS and light-emitting layer, resulting in the enhancement of luminance with a low-voltage drive. Such microscopic information and applying our method to other OLEDs will further improve the OLED performance from the microscopic viewpoint.

Organic light-emitting diodes (OLEDs) have characteristic features such as flexibility, light weight, and highly efficient electroluminescence1,2,3,4,5,6,7. Thus, they have been attracting high attention because of the application to displays such as smartphones, televisions, etc1,2,3,4,5,6,7. In 1987, Tang and VanSlyke have developed fluorescence OLEDs with tris(8-hydroxyquinolinato)aluminum (Alq3) as a luminescent material1. After that, highly efficient OLEDs using phosphorescent materials have shown that they have nearly 100% internal quantum efficiency8,9. However, blue phosphorescence OLEDs still have problems such as short lifetimes, the use of rare metals (Ir, Pt, etc.) for environmental issues, etc10. In 2009, Adachi et al. have developed OLEDs with thermally activated delayed fluorescence (TADF) as a new light-emitting mechanism11,12,13,14,15,16. TADF has an emission mechanism with not only conventional fluorescence from excited singlet states but also delayed fluorescence due to reverse intersystem crossing (RISC) from excited triplet states to excited singlet states13. This mechanism shows a high luminescence efficiency that is almost as same as that of phosphorescent OLEDs17,18,19,20.

Early OLEDs were often fabricated with a vapor deposition method, but in recent years, OLEDs have been fabricated with a solution process, which is expected to contribute to low-cost and mass production21. However, there are still rooms for clarifying the problems such as a roll-off of luminance efficiency by applying high voltages, driving lifetimes, and an overproduction of excitons by a small rate constant of RISC in TADF materials22,23,24,25,26. Clarifications by observations of electric charge states, electron orbitals, etc. at the molecular level are necessary under device operation. Although there are a lot of studies about materials and molecular design, there are few research at the microscopic point of view during the operation of OLEDs with TADF materials. Thus, it is important to directly observe the charge states in OLEDs with TADF materials from the microscopic point of view.

One of the most suitable techniques to study electric charge states in OLEDs is electron spin resonance (ESR) spectroscopy27,28. The ESR method is a highly sensitive and nondestructive technique for directly observing radicals and charges with spins in semiconductors and their devices at the molecular level. So far, we have been studying microscopic nature such as electric charge states, electron spin states, and molecular orientations in organic devices, etc. using the ESR method28,29,30,31,32,33,34,35,36,37,38,39. We have reported an ESR study of OLEDs with Alq3 to investigate the degradation mechanism, which have shown the correlation between luminescence degradation and formation of cationic species due to decomposed Alq3 molecules28. However, an operation mechanism of OLEDs has not yet been investigated using ESR under device operation from a microscopic viewpoint at a molecular level. Moreover, OLEDs with TADF materials, which show high efficiency compared to that of OLEDs with Alq3, have not yet been investigated with the ESR method. Such microscopic investigation of OLEDs with TADF materials will be useful for the development of even more efficient OLEDs.

Here, we report microscopic investigation of OLEDs with a TADF material under device operation (operando states) for the first time. We utilize 2,4,6-tris(4-9,9-dimethylacridan-10-yl)phenyl)-1,3,5-triazine (3ACR-TRZ)21 as a TADF guest material in the light-emitting layer (Fig. 1a). We study the electric charge states in OLEDs using an operando ESR method in detail. As a result, we firstly observe operando ESR signals of the OLEDs with the TADF material. We analyze the origins of the ESR signals using density functional theory calculation and clarify the dependence of the ESR intensity on applied voltage bias (Vbias) to the OLEDs. We find de-doping process of a hole transport layer and long-lived doping states in the light-emitting layer, which are useful information for understanding the operation mechanism of OLEDs with higher efficiency. These findings will be useful for fabricating and developing highly efficient and durable devices.

Materials and device structure of OLED with TADF. (a–c) Chemical structures of (a) a TADF material 3ACR-TRZ, (b) a host material CBP in the light-emitting layer, and (c) an electron transport layer (a hole blocking layer) bathocuproine (BCP). (d) A schematic of the OLED structure. (e) Energy level diagram of the materials used for the OLED.

To attain a high signal-to-noise ratio (S/N ratio) of the ESR signal by increasing the light-emitting area of the devices, we utilized a rectangular device structure (3 mm × 25 mm) in an ESR sample tube with an inner diameter of 3.5 mm33,36. Figure 1a–c shows the chemical structures of molecules used for the device fabrication. Figure 1d shows the fabricated device structure, indium tin oxide (ITO) (150 nm)/poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) (35 nm)/3ACR-TRZ(16 wt%):CBP (55 nm)/bathocuproine (BCP) (30 nm)/lithium fluoride (LiF) (1 nm)/Al (80 nm). Figure 1e shows the energy level diagram of the materials used for the OLED. The energy values of the materials except for BCP are taken from Ref.21 and those of BCP are taken from Ref.40. A film of PEDOT:PSS as a hole transport layer and a blend film of 3ACR-TRZ:CBP as a light-emitting layer were deposited on an ITO substrate with a spin-coating method. BCP, LiF, and Al were vapor-deposited sequentially on the light-emitting layer. Our device architecture is a typical one and it is important to study the typical device architecture using PEDOT:PSS, BCP, etc. because there are many examples of research on typical device architectures and their problems should be clarified11,12,13,14,15,16,17,18,19,20,21,40. The device for ESR and current density (J)-luminance measurements was sealed in an ESR sample tube with a desiccant and sealant under a nitrogen glove-box atmosphere28,36. Also, to identify the ESR signals’ origins, we fabricated thin-film samples of BCP/LiF/Al and PEDOT:PSS on nonmagnetic quartz substrates with the same fabrication method used for the OLED fabrication. The fabricated OLEDs were simultaneously measured with an ESR spectrometer (JEOL JES-FA200, X-Band 9.5 GHz) and a luminance meter (TOPCON BM-9 M) at room temperature. We used a lock-in detection method for the ESR measurements with a modulation frequency of 100 kHz for the external magnetic field. Thus, we could observe long-lived charges (spins) with a lifetime of > 10 μs or accumulated charges in the OLEDs, and cannot observe charges with a lifetime of < 10 μs that contribute the standard operation of the OLEDs28,29,30,31,36,37,38,39,41. We measured operando ESR signals while increasing Vbias from 0 to 10 V in 0.5 V increment. A standard Mn2+ marker sample was employed as a standard sample to calibrate the peak-to-peak ESR linewidth (ΔHpp) and the number of spins (Nspin) of observed ESR spectra. The Nspin was evaluated by integrating the ESR spectrum twice and by comparing the Mn2+ standard sample. More detailed fabrication methods and ESR evaluation method are described in “Methods” section.

We present the observation of operando ESR signals under device operation and compare them with simultaneously measured J and luminance L of the OLED as a function of Vbias. Figure 2a shows the Vbias dependence of the operando ESR spectra of the OLED. The electroluminescence characteristics of our fabricated OLEDs are as follows. When we fabricated devices using a conventional ITO substrate (25 mm × 25 mm), we obtained electroluminescence characteristics as shown in Supplementary Fig. S1. The light emission started at a turn-on voltage of Vbias = 4.2 V and the luminance reached 2200 cd m−2 at Vbias = 7.4 V. Here, the turn-on voltage is defined as the threshold luminance level of 1 cd m−2. The maximum current efficiency was obtained as ~ 4.5 cd A−1 at Vbias = 7.1 V, which was evaluated from the data shown in Supplementary Fig. S1a. The OLED emitted green light with at a peak wavelength of 523 nm due to the TADF material 3ACR-TRZ as shown in Supplementary Fig. S1b, which is consistent with that of the previous study21. When we fabricated devices for ESR measurements using a rectangular ITO substrate (3 mm × 25 mm, see Fig. 1d), the OLED emitted green light due to 3ACR-TRZ as shown in Supplementary Fig. S2, which is like that observed for the OLEDs fabricated with the conventional ITO substrate (25 mm × 25 mm) mentioned above. The light emission started at a turn-on voltage of Vbias = 4.5 V (Fig. 2d). The luminance reached 237 cd m−2 at Vbias = 9.5 V, and the maximum current efficiency was obtained as ~ 2.3 cd A−1 at Vbias = 6.5 V (Fig. 1d). The reason for the lower device performance obtained with the devices used for the ESR measurements may be due to the lower film quality compared to the conventional substrate used.

Operando ESR study of the TADF OLED. (a) Vbias dependence of the operando ESR spectra of the OLED. (b,c) Fitting analyses of the ESR spectra of the OLED before device operation at Vbias = 0 V (b) and after light emission at Vbias = 4.5 V (c). (d) Dependence of the number of spins (Nspin) derived from ESR spectra of the OLED and the luminance (L) of the OLED on Vbias during device operation.

We observed two variations in the ESR spectra before the light emission (0–4.0 V) and after the light emission (Vbias ≥ 4.5 V); the origins of the ESR spectra are due to long-lived charges (spins) with a lifetime of > 10 μs or accumulated charges in the OLEDs, not due to charges with a lifetime of < 10 μs that contribute the standard operation of the OLEDs, as mentioned above28,29,30,31,36,37,38,39,41. We have found that the observed ESR spectra show no anisotropy, which demonstrates that the charge-accumulation sites prove to be amorphous. We obtained the ESR parameters, g-factor and peak-to-peak ESR linewidth (ΔHpp), as g = 2.0029 ± 0.0001 and ΔHpp = 0.38 ± 0.02 mT at Vbias = 0 V, and g = 2.0029 ± 0.0001 and ΔHpp = 0.40 ± 0.02 mT at Vbias = 4.5 V, which are summarized in Supplementary Table S1.

In general, an ESR spectrum due to charges with unpaired electrons in semiconductors can be described with a Lorentzian function or a Gaussian function; while the Lorentzian function describes the states where charges are mobile, the Gaussian function describes the states where charges are immobile28,29,30,31,32,33,34,35,36,37,38,39. Since the observed ESR spectra cannot be described by a single component, we performed fitting analyses of the ESR spectra with several components using a least-squares method and two kinds of software of Igor Pro (Ver. 6.36J) and EasySpin (Ver. 5.2.18). We utilized the following Equations for the fitting analysis:

Equations (1) and (2) describes the Lorentzian and Gaussian functions, respectively. Here, we used a resonance magnetic field \(({H}_{0,\mathrm{L}}, {H}_{0,\mathrm{G}})\), a half width at half maximum \(\left({w}_{\mathrm{L}}, {w}_{\mathrm{G}}\right)\), and a spectrum height \(({h}_{\mathrm{L}}, {h}_{\mathrm{G}})\) as fitting parameters, where the subscript “L” and “G” indicate the parameters for the Lorentzian and Gaussian functions, respectively.

We start to analyze the ESR spectrum of the OLED before device operation (Vbias = 0 V). After examining the combinations of Eqs. (1) and (2), we have found the fitting curve with two components of the Lorentzian function reproduces the ESR spectrum at Vbias = 0 V. Here, the equation we used is shown below:

Figure 2b shows the fitting result of the ESR spectrum before device operation (Vbias = 0 V). Black circles in Fig. 2b show the experimental data of the ESR spectrum. A red line shows the fitting result composed of Signal A (green dotted line) and Signal B (blue dotted line). As discussed later, the origins of Signal A and Signal B are mobile charges with spins, in which case the ESR signal is well described by a Lorentzian lineshape. We obtained the ESR parameters, g-factor and ΔHpp, from the fitting result. The ESR parameters of Signal A are g = 2.0032 ± 0.0001 and ΔHpp = 0.32 ± 0.04 mT, and those of Signal B were g = 2.0028 ± 0.0001 and ΔHpp = 0.28 ± 0.04 mT. The parameters obtained from the fitting analysis are summarized in Supplementary Table S1. We have confirmed that the ESR spectra before the light emission (0 V ≤ Vbias ≤ 4.0 V) are reproduced with Signal A and Signal B. The g-factor is calculated using the magnetic resonance equation, \(h\nu =g{\mu }_{\mathrm{B}}{H}_{0}\). Here, h is the Planck constant, ν is the microwave frequency in this study, \({\mu }_{\mathrm{B}}\) is Bohr magneton, and \({H}_{0}\) is the resonance magnetic field where the ESR spectrum with first derivative form has a value of zero. The ΔHpp value is calculated from the fitting parameters as \(\Delta {H}_{\mathrm{pp}}=(2/\sqrt{3}){w}_{\mathrm{L}}\) in the Lorentz function and \(\Delta {H}_{\mathrm{pp}}=\sqrt{2}{w}_{\mathrm{G}}\) in the Gauss function, which means the difference between the two magnetic fields at a peak and valley in the ESR spectrum.

The origins of Signal A and Signal B obtained from the fitting analysis are discussed in detail in the following. First, we discuss the origin of Signal A. According to the previous studies of BCP/metal layered film samples, the formation of gap states have been reported at the BCP/metal interfaces by the interactions between metal and lowest unoccupied molecular orbital (LUMO) of BCP when the metal with a work function of ≤ 4.3 eV is used for layered films42,43. In the case of Al with a work function of 4.2 eV, a charge transfer has occurred between BCP and Al, which forms electric double layers due to the presence of gap states42,43. As a result, we have observed the ESR signal of BCP anions, and electrons can be injected into BCP from the Al metal without injection barriers43. From the observation of the motional narrowing of the ESR linewidth with a Lorentzian lineshape, we have concluded that a majority of the spins at the interfaces between BCP and Al are mobile43. In this study, we utilize the layered film of BCP/LiF/Al in the OLED structure. To investigate the effect of the insertion of LiF between BCP and Al, we fabricated a BCP/LiF/Al layered film and performed the ESR measurement. Solid line in Fig. 3a shows the ESR spectrum of the BCP/LiF/Al layered film; dashed line in Fig. 3a shows the fitting result of Signal A shown in Fig. 2a. The parameters of the observed ESR signal were g = 2.0031 ± 0.0001 and ΔHpp = 0.35 ± 0.04 mT (Supplementary Table S1). The overall features of the signal such as g-factor correspond to that of Signal A (see Fig. 3a) within experimental errors; it also accords with those of the ESR signals of the BCP/Al layered film43. The low S/N ratio of the observed signal is ascribed to the low ESR intensity of the BCP/LiF/Al layered film. In addition, it has been reported that BCP films show no ESR signal43. Moreover, we confirm that LiF films show no ESR signal. Furthermore, the Lorentzian lineshape of Signal A is consistent with that of the layered films of BCP/Al and BCP/LiF/Al43. Therefore, we demonstrate that the origin of Signal A obtained from the fitting analysis is due to the gap states at the BCP/LiF/Al interface.

ESR spectra of layered films and ESR variation of the OLED. (a) ESR spectrum of a BCP/LiF/Al layered film. (b) ESR spectrum of a PEDOT:PSS layered film. (c) ESR spectra of the OLED before light emission at Vbias = 4.0 V and after light emission at Vbias = 4.5 V. (d) Difference in ESR spectra at Vbias = 4.5 V and 4.0 V.

The origin of Signal B is discussed as follows. It has been reported that holes (positive polarons) in PEDOT:PSS are generated because hole doping happens in PEDOT by PSS and thus an ESR signal of PEDOT:PSS is observed33,41. The holes in PEDOT are mobile, which gives the ESR signal with a Lorentzian lineshape33. In this study, since we used the PEDOT:PSS film as the hole transport layer in the OLED, we performed the ESR measurement of a PEDOT:PSS film to confirm the contribution of PEDOT:PSS to the ESR signals of the OLED. As a result, the ESR parameters were obtained from the ESR spectrum of the PEDOT:PSS layer as g = 2.0028 ± 0.0001 and ΔHpp = 0.28 ± 0.03 mT, as shown in solid line in Fig. 3b. We find that these parameter values (g-factor and ΔHpp) and peak-to-peak ESR intensity of the PEDOT:PSS film almost accord with those of Signal B (see dashed line in Figs. 3b and 2b). Therefore, the origin of Signal B is found to be holes in PEDOT:PSS in the OLED.

Next, we analyze the ESR spectra after the light emission (Vbias ≥ 4.5 V). Figure 3c shows the comparison between before (Vbias = 4.0 V) and after (Vbias = 4.5 V) the light emission. We find that the intensity of the spectrum at Vbias = 4.5 V is larger than that of the spectrum at Vbias = 4.0 V. Also, as shown in Fig. 3c, the lineshape of the signal at Vbias = 4.5 V is slightly different from that at Vbias = 4.0 V, with a component slightly shifted toward the high magnetic field side. In other words, simply increasing the intensity of the signal at Vbias = 4.0 V does not reproduce the signal at Vbias = 4.5 V. This means that another component is present in the signal at Vbias = 4.5 V. Figure 3d shows the difference spectrum between the two spectra. The ESR parameters of the difference spectrum were obtained as g = 2.0030 ± 0.0001 and ΔHpp = 0.40 ± 0.04 mT. The ESR spectra at Vbias > 4.5 V were as large as that at Vbias = 4.5 V and we have observed the similar difference in ESR spectra at higher voltages such as 6.0 V and 4.0 V, as mentioned above (see Supplementary Fig. S3). Thus, we newly define this difference spectrum as Signal C, which are listed in Supplementary Table S1. Although the g-factor of Signal C appears to be close to those of Signal A and Signal B, the g-factor and ΔHpp can be distinguished from those of Signal A and Signal B (see Fig. 2c and Supplementary Table S1). These results support the existence of Signal C. Figure 2c shows the result of the fitting analysis for the ESR spectrum (Vbias = 4.5 V) after the light emission. We can reproduce the ESR spectra after the light emission using 3 components, that is, Signal A due to the generating gap states at the BCP/LiF/Al interface, Signal B due to holes in the PEDOT:PSS film, and Signal C obtained from the differential spectrum between those at Vbias = 4.5 V and 4.0 V. Since Signal C is observed after the light emission and is different from those of the BCP/LiF/Al layered film (Signal A) and PEDOT:PSS film (Signal B), which are materials except for the light-emitting layer in the OLED, it is supposed that the origin of Signal C is related with spins of charges in the light-emitting layer. To further confirm the origin of Signal C, we performed an ESR study of a 3ACR-TRZ:CBP film used as the light-emitting layer. As a result, no ESR signal was observed at room temperature, which means that neutral molecules of 3ACR-TRZ and CBP do not have spins. Thus, Signal C can only be observed when charge doping is performed, as discussed below.

To investigate the origin of Signal C in detail, we performed density functional theory (DFT) calculation with Gaussian 09. The molecules for the calculation are 3ACR-TRZ and CBP used for the light-emitting layer. We calculated g-factors of the cationic and anionic states for the two molecules, respectively. Here, we performed the DFT calculation with structure optimization using a functional UB3LYP with a basis function 6-31+G(d,p). In the g-tensor calculation, we define the coordinate axes of x-, y-, and z-axis as shown in Supplementary Fig. S4. Since an anisotropy of the g-factor was not observed in the ESR measurements, the materials with observed spins are found to have no molecular orientation. Thus, we calculated an averaged g-factor (gave) of the principal values (gx, gy, gz) of the g-tensor components as \({g}_{\mathrm{ave}}= \sqrt{\left({g}_{x}^{2}+{g}_{y}^{2}+{g}_{z}^{2}\right)/3}\). As a result, the gave of cationic 3ACR-TRZ and cationic CBP is determined as gave = 2.00289 and gave = 2.00297, and that of anionic 3ACR-TRZ and anionic CBP is determined as gave = 2.00275 and gave = 2.00258, respectively. The calculation results are summarized in Table 1. The g-factor (g = 2.0030) obtained from Fig. 3d is consistent with the gave of cationic CBP (gave = 2.00297). The gave values of both anionic states of 3ACR-TRZ and CBP are not consistent with the gave of cationic CBP (see Table 1). Therefore, the origin of Signal C is found to be due to long-lived or accumulated holes (cations) of CBP in the light-emitting layer after the hole transfer from the PEDOT:PSS layer to the light-emitting layer along with the start of the light emission. The spin density distributions for the cationic and anions states of 3ACR-TRZ and CBP were calculated by the DFT method as shown in Supplementary Fig. S4. Supplementary Fig. S4b,c show the spin density distribution of the cationic and anionic states of 3ACR-TRZ, respectively. We confirm that the spin density distribution of three acridan (ACR) units and one triazine (TRZ) unit is separated. Since the torsion angle between ACR and TRZ is nearly 90 degrees by steric hindrance, the localization and separation of spin density occur as known for highest occupied molecular orbital (HOMO) and LUMO of 3ACR-TRZ21. Supplementary Fig. S4e,f show the spin density distribution of the cationic and anionic states of CBP, respectively. Since CBP has a plane molecular structure, spins are delocalized and widely distributed in CBP.

The relation between the ESR characteristics and luminance of the OLED is an interesting issue to investigate the effect of internal charge states in the OLED on the performance of the OLED. Figure 2d shows the Vbias dependence of Nspin derived from the ESR signal of the OLED and the luminance (L) observed during the ESR measurements. We find that Nspin decreases with the rise in Vbias before the light emission (Vbias = 0–4.0 V). The reason for the Nspin decrease will be discussed in detail later. In addition, we confirm that the Nspin rapidly increases at Vbias = 4.5 V in comparison to that at Vbias = 4.0 V. This Nspin increase seems to relate with Signal C as discussed above, which is partially ascribed to the formation of long-lived or accumulated cations of CBP with a lifetime of > 10 μs in the light-emitting layer after the light emission (Vbias ≥ 4.5 V). We comment that the Nspin number is given in absolute value in this study because in the device structure of this experiment, spins present in the PEDOT:PSS layer, light-emitting layer, and BCP/LiF/Al layer with different areas are observed, as shown in Fig. 1d, and the Nspin per unit area of the active layer cannot be defined.

Interestingly, we observe a gradual decrease in Nspin before the light emission with the rise in Vbias after device operation (0 < Vbias ≤ 4.0 V) in contrast to the case after the light emission (Vbias ≥ 4.5 V) as shown in Fig. 2d. There are two likely reasons for the Nspin decrease. One reason may be the recombination between holes (positive polarons) in the PEDOT:PSS layer and leakage electrons injected from the cathode passed through the light-emitting layer by Vbias; we will discuss this first reason in more detail later. Another reason may be the formation of bipolarons by increasing the polaron density in the PEDOT:PSS layer44,45,46,47,48, where a bipolaron is the combination of two polarons and has no spin44,45,46,47,48. However, the latter reason will be ruled out later by the following results for OLEDs with MoO3. Also, the low hole density of PEDOT:PSS in the OLED before light emission seems to support this exclusion.

To clarify the reason for the Nspin decrease in the OLED before the light emission in detail, we performed an operando ESR measurements of the OLED with a further electron blocking layer MoO3; the experimental results are shown in Fig. 4. The actual composition of molybdenum oxide may be MoO3−x where x represents the amount of oxygen defects but will be denoted MoO3 for simplicity. We fabricated the OLED in which we inserted a MoO3 layer between the PEDOT:PSS layer and light-emitting layer (Fig. 4a,b), and studied the Vbias dependence of the ESR spectra and Nspin (Fig. 4c,d). The component structure of OLEDs with the electron blocking layer MoO3 is ITO (150 nm)/PEDOT:PSS (35 nm)/MoO3 (7.5 nm)/3ACR-TRZ(16 wt%):CBP (55 nm)/BCP (30 nm)/LiF (1 nm)/Al (80 nm), which is the same structure mentioned in the above results and discussion except for the MoO3 insertion. The energy levels of the conduction band minimum (CBM) (− 2.3 eV) and valence band maximum (VBM) (− 5.3 eV) of MoO3 in Fig. 4b are taken from Refs.31,49,50,51, where MoO3 acts as a hole-transport layer connected with Ag hole collecting electrodes31,49,50,51. The energy level of the CBM of MoO3 (− 2.3 eV) is shallower than the LUMO levels of the light-emitting layer (Fig. 4b). Also, the CBM of MoO3 is thought to be shallower than the LUMO level of PEDOT:PSS (− 2.4 eV)52. Thus, MoO3 can play a role of a further electron blocking layer, which further prevents the leakage electron transfer from the light-emitting layer to the PEDOT:PSS layer. MoO3 was used because of its resistance to organic solvents. This layer serves as a substrate when spin-coating the light-emitting layer. If tris(4-carbazoyl-9-ylphenyl)amine (TCTA) or N,N'-diphenyl-N,N'-bis(1-naphthyl)-1,1'-biphenyl-4,4'-diamine (α-NPD or NPB) were used, they could dissolve during spin-coating of the light-emitting layer. MoO3 is a metal oxide and not an organic material. Therefore, the thickness of the MoO3 film is important, and in this study, a thickness of 7.5 nm, which is commonly used as a hole transport layer in organic solar cells31,49, was adopted. For the energy levels of MoO3, deeper energy levels of CBM (− 6.6 or − 6.7 eV) and VBM (− 9.6 or − 9.7 eV) than those in Fig. 4b have been reported, where the electron blocking ability of MoO3 with the very deep Fermi level is thought to be excellent53,54.

Device structure and operando ESR study of OLED with MoO3. (a) Schematic structure of the OLED with MoO3. (b) Energy level diagram of the OLED with MoO3. (c) Vbias dependence of the operando ESR spectra of the OLED with MoO3. (d) Dependence of Nspin derived from ESR spectra and the luminance (L) of the OLED with MoO3 on Vbias during device operation.

The electroluminescence characteristics of the OLEDs with MoO3 are as follows. When we fabricated devices using the conventional ITO substrate (25 mm × 25 mm), we obtained electroluminescence characteristics as shown in Supplementary Fig. S5. The luminance reached 19,145 cd m−2 at Vbias = 10.0 V. The maximum current efficiency was obtained as ~ 12.8 cd A−1 at Vbias = 7.8 V, which was evaluated from the data shown in Supplementary Fig. S5. The OLED emitted green light due to 3ACR-TRZ as observed for the OLEDs without MoO3 mentioned above. These characteristics are similar to those of the previous study21. When we fabricated devices for ESR measurements using the rectangular ITO substrate (3 mm × 25 mm, see Fig. 1d), the OLED emitted green light due to 3ACR-TRZ, which is like that observed for the OLEDs fabricated with the conventional ITO substrate (25 mm × 25 mm) mentioned above. The turn-on voltage was Vbias = 3.1 V, and the luminance reached 1245 cd m−2 at Vbias = 8.5 V. The maximum current efficiency was obtained as ~ 6.4 cd A−1 at Vbias = 7.5 V (Fig. 4d). The reason for the lower device performance obtained with the devices used for the ESR measurements may be due to the lower film quality compared to the conventional substrate used. Figure 4c shows the Vbias dependence of ESR spectra of the OLED with MoO3 before and after the light emission. These ESR spectra are not described by the single component as in the case of the OLED without MoO3, and thus we analyzed the ESR spectra before and after the light emission with the same fitting method used for the case of the OLED without MoO3. The fitting results are shown in Supplementary Fig. S6 and Supplementary Table S1. As in the case of the OLED without MoO3, we find that the ESR spectra are reproduced by the fitting curve with 2 components of Lorentzian (Signal A and Signal B) and 3 components of Lorentzian (Signal A, Signal B, and Signal C) before and after the light emission, respectively. Thus, the insertion of the MoO3 layer is found to have no large effect on the ESR signals. Figure 4d shows the Vbias dependence of Nspin evaluated from the observed ESR spectra. From Fig. 4d, we confirm that the decrease in Nspin before the light emission is suppressed in contrast to that without MoO3 shown in Fig. 2d. That is, by inserting the MoO3 layer, the leakage electron transfer from the light-emitting layer to the PEDOT:PSS layer is prevented, and the charge recombination between holes in the PEDOT:PSS layer and electrons leaked from the light-emitting layer is suppressed.

In addition, since the energy level of the VBM of MoO3 is located between the work function of the PEDOT:PSS layer and the HOMO levels of the light-emitting layer, it is thought that the hole injection from the PEDOT:PSS layer to the light-emitting layer smoothly occurs. That is, the charge recombination between holes and electrons in the light-emitting layer is expected to efficiently occur by inserting MoO3. In fact, the turn-on voltage of the OLED with MoO3 was Vbias = 3.1 V, which was 1.4 V less than that without MoO3. We newly find that MoO3 has a function of electron blocking layer in the OLED with the PEDOT:PSS hole transport layer, which performs a low-voltage drive. At Vbias > 3.1 V, we observe that the Nspin tends to increase by generating long-lived holes in CBP in the light-emitting layer similarly observed for Fig. 2d. Moreover, we observe an enhancement of the luminance for the OLED with MoO3 compared to that without MoO3 (see Figs. 4d and 2d). This luminance enhancement is reasonably ascribed to the electron blocking effect by the MoO3 layer mentioned above. It has been reported that performance of OLEDs is improved by optimizing the thickness of a hole-injection layer of MoO3 inserted between ITO and α-NPD (or NPB)55. For the device structure used in this study, optimization of the MoO3 film thickness may also provide further improvement of device characteristics, and it will be interesting to study the detailed MoO3 film-thickness dependence of ESR characteristics and device properties in the future. We comment the decrease in Nspin at Vbias ≥ 7.0 V, which may be caused by the charge recombination between holes in the PEDOT:PSS layer and electrons leaked from the light-emitting layer at higher Vbias, as mentioned above.

We fabricated the OLEDs with the TADF material 3ACR-TRZ and performed the operando ESR measurements to clarify the internal charge states in the OLEDs in detail. As a result, we have observed the variations of the ESR spectra of the OLEDs during the device operation. The experimental ESR spectrum of the OLED before the light emission was well reproduced by the two-component fitting (Signal A and Signal B). Signal A originated from the gap states at the BCP/LiF/Al interface, while Signal B from holes in the PEDOT:PSS layer. After the light emission, we have newly observed the ESR signal (Signal C) due to the long-lived or accumulated cations in CBP in the light-emitting layer. Moreover, by observing the Vbias dependence of the Nspin in the OLEDs, the decrease of Nspin has been confirmed.

To investigate the reason for the Nspin decrease in detail, we fabricated the OLEDs with MoO3 that is inserted between the PEDOT:PSS and light-emitting layers, and performed the operando ESR measurements. As a result, we have revealed that the charge recombination in the PEDOT:PSS layer with leakage electrons from the light-emitting layer causes the Nspin decrease and the high turn-on voltage of the light emission. In other words, the effect of the leakage electrons during driving the OLEDs has been verified at the molecular level by using the ESR method. In this study, no TADF-derived ESR signal was observed in the OLEDs using TADFs. This is different from the results of our previous OLEDs using the fluorescent material Alq3 (Ref.28). In that study, an Alq3-derived ESR signal was observed28. Therefore, these results may suggest that OLEDs with TADFs are superior to OLEDs with fluorescent materials in terms of suppressing charge formation and accumulation in light-emitting materials. The information obtained in this study will be useful for other materials and devices and be helpful to developments of OLED design with high efficiency and low driving voltage of the light emission. The leakage current affects not only TADF OLEDs but also fluorescent or phosphorescent OLEDs. Therefore, the findings of this study are important not only for TADF OLEDs but also for the development of fluorescent or phosphorescent OLEDs.

OLEDs for ESR measurements were fabricated using an ITO substrate with an active layer of 2.4 mm × 14 mm = 33.6 mm2. The ITO substrates were cleaned by ultrasonic cleaning with 2-propanole and acetone for 5 min and UV ozone cleaning for 30 min, respectively. After that, the PEDOT:PSS (Clevious AI4083) layer was spin-coated on the ITO substrate at 4000 rpm for 30 s and dried at 120 °C for 10 min. To form the light-emitting layer, 3ACR-TRZ was mixed with CBP and dissolved in 2 mL of chloroform. The mass ratio of 3ACR-TRZ and CBP was 1.6:8.4 and the combined weight was totally 10 mg. The dissolved solution was stirred with a stirring tip for more than 30 min. The light-emitting layer was then spin-coated at 1500 rpm for 30 s on the substrates and dried at 80 °C for 30 min. The electron transport layer (BCP), the electron injection layer (LiF), and the cathode (Al) were sequentially deposited by a vacuum deposition method at a pressure of 1.0 × 10−5 Pa. The deposition rate of BCP, LiF, and Al was 1.0–2.0 Å s−1, 0.1 Å s−1, and 5–20 Å s−1, respectively. In the case of the OLED inserting MoO3, the MoO3 layer was deposited between the PEDOT:PSS layer and the light-emitting layer. The thickness of MoO3 was 7.5 nm, and the deposition rate was 0.5 Å s−1 at a pressure of 1 × 10−5 Pa. The other layers were fabricated with the same method used for the OLEDs without MoO3.

ESR measurements were performed with a rise of applied voltage bias (Vbias) from 0 to 10 V with an increment of 0.5 V at room temperature. When the ESR measurements were performed, we integrated the ESR spectra at each Vbias for 15 times. The calibration of the g-factor was performed with a software program by a JEOL ESR system taking secondary high-order correction towards valid resonance magnetic field into account. The peak-to-peak ESR linewidth was evaluated by the difference between the two magnetic fields at a peak and valley of the ESR spectrum. The number of the spins (Nspin) was calculated by the double integration of an ESR spectrum considering the absolute value of the Nspin of a standard Mn2+ marker sample that is calibrated with another standard sample of a solution (220 µL) of 4-Hydroxy-2,2,6,6-tetramethylpiperidine 1-oxyl (TEMPOL).

The datasets used and/or analyzed during the current study available from the corresponding author on reasonable request.

Tang, C. W. & VanSlyke, S. A. Organic electroluminescent diodes. Appl. Phys. Lett. 51, 913–915 (1987).

Article CAS ADS Google Scholar

Sugimoto, A. et al. Flexible OLED displays using plastic substrates. IEEE J. Sel. Top. Quantum Electron. 10, 107–114 (2004).

Article CAS ADS Google Scholar

Kim, S.-Y. et al. A study on the characteristics of OLEDs using Ir complex for blue phosphorescence. Curr. Appl. Phys. 7, 380–383 (2007).

Article ADS Google Scholar

Cai, M. et al. High-efficiency solution-processed small molecule electrophosphorescent organic light-emitting diodes. Adv. Mater. 23, 3590–3596 (2011).

Article CAS PubMed Google Scholar

Tagare, J. & Vaidyanathan, S. Recent development of phenanthroimidazole-based fluorophores for blue organic light-emitting diodes (OLEDs): An overview. J. Mater. Chem. C 6, 10138–10173 (2018).

Article CAS Google Scholar

Cebrián, C. & Mauro, M. Recent advances in phosphorescent platinum complexes for organic light-emitting diodes. Beilstein J. Org. Chem. 14, 1459–1481 (2018).

Article PubMed PubMed Central Google Scholar

Komatsu, R., Sasabe, H., Inomata, S., Pu, Y.-J. & Kido, J. High efficiency solution processed OLEDs using a thermally activated delayed fluorescence emitter. Synth. Met. 202, 165–168 (2015).

Article CAS Google Scholar

Adachi, C., Baldo, M. A., Thompson, M. E. & Forrest, S. R. Nearly 100% internal phosphorescence efficiency in an organic light-emitting device. J. Appl. Phys. 90, 5048–5051 (2001).

Article CAS ADS Google Scholar

Kawamura, Y. et al. 100% phosphorescence quantum efficiency of Ir(III) complexes in organic semiconductor films. Appl. Phys. Lett. 86, 071104 (2005).

Article ADS Google Scholar

Zhang, Y., Lee, J. & Forrest, S. R. Tenfold increase in the lifetime of blue phosphorescent organic light-emitting diodes. Nat. Commun. 5, 5008 (2014).

Article CAS PubMed ADS Google Scholar

Endo, A. et al. Thermally activated delayed fluorescence from Sn4+-porphyrin complexes and their application to organic light emitting diodes—a novel mechanism for electroluminescence. Adv. Mater. 21, 4802–4806 (2009).

Article CAS PubMed Google Scholar

Tanaka, H., Shizu, K., Miyazaki, H. & Adachi, C. Efficient green thermally activated delayed fluorescence (TADF) from a phenoxazine–triphenyltriazine (PXZ–TRZ) derivative. Chem. Commun. 48, 11392 (2012).

Article CAS Google Scholar

Uoyama, H., Goushi, K., Shizu, K., Nomura, H. & Adachi, C. Highly efficient organic light-emitting diodes from delayed fluorescence. Nature 492, 234–238 (2012).

Article CAS PubMed ADS Google Scholar

Nakanotani, H., Masui, K., Nishide, J., Shibata, T. & Adachi, C. Promising operational stability of high-efficiency organic light-emitting diodes based on thermally activated delayed fluorescence. Sci. Rep. 3, 2127 (2013).

Article CAS PubMed PubMed Central ADS Google Scholar

Tanaka, H., Shizu, K., Nakanotani, H. & Adachi, C. Twisted intramolecular charge transfer state for long-wavelength thermally activated delayed fluorescence. Chem. Mater. 25, 3766–3771 (2013).

Article CAS Google Scholar

Nasu, K. et al. A highly luminescent spiro-anthracenone-based organic light-emitting diode exhibiting thermally activated delayed fluorescence. Chem. Commun. 49, 10385 (2013).

Article CAS Google Scholar

Kaji, H. et al. Purely organic electroluminescent material realizing 100% conversion from electricity to light. Nat. Commun. 6, 8476 (2015).

Article CAS PubMed ADS Google Scholar

Yang, Z. et al. Recent advances in organic thermally activated delayed fluorescence materials. Chem. Soc. Rev. 46, 915–1016 (2017).

Article CAS PubMed Google Scholar

Zeng, W. et al. Achieving nearly 30% external quantum efficiency for orange-red organic light emitting diodes by employing thermally activated delayed fluorescence emitters composed of 1,8-naphthalimide-acridine hybrids. Adv. Mater. 30, 1704961 (2018).

Article Google Scholar

Etherington, M. K. et al. Persistent dimer emission in thermally activated delayed fluorescence materials. J. Phys. Chem. C 123, 11109–11117 (2019).

Article CAS Google Scholar

Wada, Y. et al. Highly efficient electroluminescence from a solution-processable thermally activated delayed fluorescence emitter. Appl. Phys. Lett. 107, 183303 (2015).

Article ADS Google Scholar

Kawamura, Y., Sasabe, H. & Adachi, C. Simple accurate system for measuring absolute photoluminescence quantum efficiency in organic solid-state thin films. Jpn. J. Appl. Phys. 43, 7729–7730 (2004).

Article CAS ADS Google Scholar

Inoue, M. et al. Effect of reverse intersystem crossing rate to suppress efficiency roll-off in organic light-emitting diodes with thermally activated delayed fluorescence emitters. Chem. Phys. Lett. 644, 62–67 (2016).

Article CAS ADS Google Scholar

Hosokai, T. et al. Evidence and mechanism of efficient thermally activated delayed fluorescence promoted by delocalized excited states. Sci. Adv. 3, e1603282 (2017).

Article PubMed PubMed Central ADS Google Scholar

Wada, Y., Nakagawa, H., Matsumoto, S., Wakisaka, Y. & Kaji, H. Organic light emitters exhibiting very fast reverse intersystem crossing. Nat. Photon. 14, 643–649 (2020).

Article CAS ADS Google Scholar

Zhang, D. et al. Highly efficient and stable blue organic light-emitting diodes based on thermally activated delayed fluorophor with donor-void-acceptor motif. Adv. Sci. 9, 2106018 (2022).

Article CAS Google Scholar

Pawlik, T. D., Kondakov, D. Y., Begley, W. J. & Young, R. H. Charge carriers and charge-transfer reactions in OLED devices studied by electron paramagnetic resonance. J. Soc. Inf. Disp. 18, 277 (2010).

Article CAS Google Scholar

Sato, G. et al. Direct observation of radical states and the correlation with performance degradation in organic light-emitting diodes during device operation. Phys. Status Solidi 215, 1700731 (2018).

Article ADS Google Scholar

Marumoto, K., Kuroda, S., Takenobu, T. & Iwasa, Y. Spatial extent of wave functions of gate-induced hole carriers in pentacene field-effect devices as investigated by electron spin resonance. Phys. Rev. Lett. 97, 256603 (2006).

Article PubMed ADS Google Scholar

Watanabe, T., Yamanari, T. & Marumoto, K. Deterioration mechanism of perovskite solar cells by operando observation of spin states. Commun. Mater. 1, 96 (2020).

Article Google Scholar

Xue, D., Saito, M., Osaka, I. & Marumoto, K. Stability improvement mechanism due to less charge accumulation in ternary polymer solar cells. npj Flex. Electron. 6, 22 (2022).

Article CAS Google Scholar

Son, D., Marumoto, K., Kizuka, T. & Shimoi, Y. Electron spin resonance of thin films of organic light-emitting material tris(8-hydroxyquinoline) aluminum doped by magnesium. Synth. Met. 162, 2451–2454 (2012).

Article CAS Google Scholar

Marumoto, K., Fujimori, T., Ito, M. & Mori, T. Charge formation in pentacene layers during solar-cell fabrication: Direct observation by electron spin resonance. Adv. Energy Mater. 2, 591–597 (2012).

Article CAS Google Scholar

Son, D., Shimoi, Y., Kizuka, T. & Marumoto, K. Direct observation of charge carriers in highly magnesium-doped tris(8-hydroxyquinoline) aluminum thin film by electron spin resonance. Jpn. J. Appl. Phys. 52, 05DB07 (2013).

Article Google Scholar

Son, D., Shimoi, Y. & Marumoto, K. Study on n-type doped electron-transporting layers in OLEDs by electron spin resonance. Mol. Cryst. Liq. Cryst. 599, 153–156 (2014).

Article CAS Google Scholar

Son, D., Kuwabara, T., Takahashi, K. & Marumoto, K. Direct observation of UV-induced charge accumulation in inverted-type polymer solar cells with a TiOx layer: Microscopic elucidation of the light-soaking phenomenon. Appl. Phys. Lett. 109, 133301 (2016).

Article ADS Google Scholar

Kubodera, T. et al. Operando direct observation of charge accumulation and the correlation with performance deterioration in PTB7 polymer solar cells. ACS Appl. Mater. Interfaces 10, 26434–26442 (2018).

Article CAS PubMed Google Scholar

Rachmat, V. A. S. A., Kubodera, T., Son, D., Cho, Y. & Marumoto, K. Molecular oriented charge accumulation in high-efficiency polymer solar cells as revealed by operando spin analysis. ACS Appl. Mater. Interfaces 11, 31129–31138 (2019).

Article CAS PubMed Google Scholar

Osawa, F. & Marumoto, K. Operando direct observation of spin-states and charge-trappings of blue light-emitting-diode materials in thin-film devices. Sci. Rep. 10, 18800 (2020).

Article CAS PubMed PubMed Central ADS Google Scholar

Toyoshima, S. et al. Electronic structure of bathocuproine on metal studied by ultraviolet photoemission spectroscopy. Jpn. J. Appl. Phys. 46, 2692–2695 (2007).

Article CAS ADS Google Scholar

Nagamori, T. & Marumoto, K. Direct observation of hole accumulation in polymer solar cells during device operation using light-induced electron spin resonance. Adv. Mater. 25, 2362–2367 (2013).

Article CAS PubMed Google Scholar

Sakurai, T. et al. Influence of gap states on electrical properties at interface between bathocuproine and various types of metals. J. Appl. Phys. 107, 043707 (2010).

Article ADS Google Scholar

Matsuo, Y., Son, D., Shimoi, Y. & Marumoto, K. Direct observation of spins at bathocuproine (BCP) interfaces: An electron spin resonance study on BCP/metal (Al or Au) thin films. Chem. Phys. Lett. 607, 29–33 (2014).

Article CAS ADS Google Scholar

Scott, J. C., Pfluger, P., Krounbi, M. T. & Street, G. B. Electron-spin-resonance studies of pyrrole polymers: Evidence for bipolarons. Phys. Rev. B 28, 2140–2145 (1983).

Article CAS ADS Google Scholar

Heeger, A. J., Kivelson, S., Schrieffer, J. R. & Su, W. P. Solitons in conducting polymers. Rev. Mod. Phys. 60, 781–850 (1988).

Article CAS ADS Google Scholar

Tsuji, M. et al. Two-dimensional magnetic interactions and magnetism of high-density charges in a polymer transistor. Appl. Phys. Lett. 102, 133301 (2013).

Article ADS Google Scholar

Sakurai, Y., Matsumoto, D. & Marumoto, K. Electrically controlled dimensionality of magnetic systems in organic materials. Appl. Magn. Reson. 49, 767–782 (2018).

Article CAS Google Scholar

Iguchi, S., Sakurai, Y., Fujita, N., Osawa, F. & Marumoto, K. Electrically controllable spin states of holes and electrons in organic semiconductor materials. ACS Appl. Electron. Mater. 1, 2522–2530 (2019).

Article CAS Google Scholar

Vohra, V. et al. Efficient inverted polymer solar cells employing favourable molecular orientation. Nat. Photon. 9, 403–408 (2015).

Article CAS ADS Google Scholar

Yin, Z. et al. Bandgap tunable Zn1-xMgxO thin films as highly transparent cathode buffer layers for high-performance inverted polymer solar cells. Adv. Energy Mater. 4, 1301404 (2014).

Article Google Scholar

Yin, Z., Wei, J. & Zheng, Q. Interfacial materials for organic solar cells: Recent advances and perspectives. Adv. Sci. 3, 1500362 (2016).

Article Google Scholar

Yang, Y. et al. Spectral-resolving capable and integratable multilayered conductive films via an inkjet method. J. Mater. Chem. C 1, 1739–1744 (2013).

Article CAS ADS Google Scholar

Kröger, M. et al. Role of the deep-lying electronic states of MoO3 in the enhancement of hole-injection in organic thin films. Appl. Phys. Lett. 95, 123301 (2009).

Article ADS Google Scholar

Schulz, P. et al. High-work-function molybdenum oxide hole extraction contacts in hybrid organic-inorganic perovskite solar cells. ACS Appl. Mater. Interfaces 8, 31491–31499 (2016).

Article CAS PubMed Google Scholar

Matsushima, T., Jin, G. H. & Murata, H. Marked improvement in electroluminescence characteristics of organic light-emitting diodes using an ultrathin hole-injection layer of molybdenum oxide. J. Appl. Phys. 104, 054501 (2008).

Article ADS Google Scholar

Download references

This work was partially supported by JSPS KAKENHI (Grant Numbers JP19K21955 and JP20H05840 (Grant-in-Aid for Transformative Research Areas, “Dynamic Exciton”)), Japan; JST PRESTO, Japan; Iketani Science and Technology Foundation, Japan; Iwatani Naoji Foundation, Japan; JST ALCA (Grant Number JPMJAL1603), Japan; JST MIRAI (Grant Numbers JPMJMI20C5, JPMJMI22C1, and JPMJMI22E2), Japan; NEDO Green Innovation, Japan.

Department of Materials Science, Institute of Pure and Applied Sciences, University of Tsukuba, Tsukuba, Ibaraki, 305-8573, Japan

Shintaro Yumoto, Junya Katsumata, Fumiya Osawa & Kazuhiro Marumoto

Institute for Chemical Research, Kyoto University, Uji, Kyoto, 611-0011, Japan

Yoshimasa Wada, Katsuaki Suzuki & Hironori Kaji

Tsukuba Research Center for Energy Materials Science (TREMS), University of Tsukuba, Ibaraki, 305-8571, Japan

Kazuhiro Marumoto

You can also search for this author in PubMed Google Scholar

S.Y. and K.M. conceived and designed the study. S.Y., J.K., and F.O. fabricated all the samples, performed the experiments, analyzed the data. S.Y. and K.M. wrote the manuscript. 3ACR-TRZ were synthesized by Y.W., K.S., and H.K. K.M supervised this work. All authors discussed the results and reviewed the manuscript.

Correspondence to Kazuhiro Marumoto.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Yumoto, S., Katsumata, J., Osawa, F. et al. Operando ESR observation in thermally activated delayed fluorescent organic light-emitting diodes. Sci Rep 13, 11109 (2023). https://doi.org/10.1038/s41598-023-38063-3

Download citation

Received: 27 April 2023

Accepted: 02 July 2023

Published: 10 July 2023

DOI: https://doi.org/10.1038/s41598-023-38063-3

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.